Korean Journal of Chemical Engineering, Vol.36, No.10, 1724-1731, October, 2019
Effect of petroleum pitch coating on electrochemical performance of graphite as anode materials
E-mail:
The electrochemical characteristics of artificial graphite coated with petroleum pitch were investigated as anode material in lithium ion batteries. Petroleum pitch with various softening points (SP 150, 200 and 250 °C) was prepared to coat the surface of artificial graphite using tetrahydrofuran as the solvent. Scanning electron microscopy and transmission electron microscopy were used to confirm the coating properties of the prepared anode materials. The electrochemical characteristics of the batteries were investigated by initial charge/discharge, cycle, rate performance, cyclic voltammetry and electrochemical impedance spectroscopy tests in the electrolyte of 1.0M LiPF6 (EC :DEC= 1 : 1 vol%). With the goal of optimizing the pitch coating process of graphite as an anode material, both the composition ratios of artificial graphite to petroleum pitch and the carbonization temperatures were varied. The best battery anode performance was found to be 10wt% coated carbon with heat treatment at 1,000 °C on the artificial graphite using petroleum pitch with SP 250 °C. Pitch-derived amorphous carbon coating effectively decreases irreversible capacity and increases the cycle stability. The prepared anode materials have good initial efficiency (92.9%), discharge capacity (343 mAh/g), cycle stability (97%), and rate performance of 10 C/0.1 C (84.1%).
- Ko HS, Kim JH, Wang J, Lee JD, J. Power Sources, 372, 107 (2017)
- Ko HS, Park HW, Lee JD, Korean Chem. Eng. Res., 56(5), 718 (2018)
- Lee SH, Lee JD, Korean Chem. Eng. Res., 56(4), 561 (2018)
- Han YJ, Kim J, Yeo JS, An JC, Hong IP, Nakabayashi K, Miyawaki J, Jung JD, Yoon SH, Carbon, 94, 432 (2015)
- Liu SH, Ying Z, Wang ZM, Li F, Bai S, Wen L, Chemg HM, NEW CARBON MATERIALS, 23(1), 30 (2008)
- Ohta N, Nagaoka K, Hoshi K, Bitoh S, Inagaki M, J. Power Sources, 194(2), 985 (2009)
- Li H, Zhou H, Chem. Commun., 48, 1201 (2012)
- Kim BH, Kim JH, Kim JG, Bae MJ, Im JS, Lee CW, Kim S, J. Ind. Eng. Chem., 41, 1 (2016)
- Ko HS, Choi JE, Lee JD, Appl. Chem. Eng., 25(6), 592 (2014)
- Jo YJ, Lee JD, Korean Chem. Eng. Res., 57(1), 5 (2019)
- Lee ML, Li YH, Liao SC, Chen JM, Yeh JW, Shih HC, Electrochim. Acta, 112, 529 (2013)
- Yoon S, Kim H, Oh SM, J. Power Sources, 94(1), 68 (2001)
- Nozaki H, Nagaoka K, Hoshi K, Ohta N, Inagaki M, J. Power Sources, 194(1), 486 (2009)
- Kim JG, Kim JH, Im JS, Lee YS, Bae TS, J. Ind. Eng. Chem., 62, 176 (2018)
- Seo SW, Choi YJ, Kim JH, Cho JH, Lee YS, Im JS, Catal. Lett., 29, 385 (2019)
- Zhang HL, Li F, Liu C, Cheng HM, J. Phys. Chem. C, 112, 7767 (2008)
- Han YJ, Hwang JU, Kim KS, Kim JH, Lee JD, Im JS, J. Ind. Eng. Chem., 73, 241 (2019)
- Kim JG, Kim JH, Song BJ, Lee CW, Im JS, J. Ind. Eng. Chem., 36, 293 (2016)
- Mabuchi A, TANSO, 65, 298 (1994)
- Kim BH, Kim JH, Kim JG, Im JS, Lee CW, Kim S, J. Ind. Eng. Chem., 45, 99 (2017)
- Wang C, Zhao H, Wang J, Wang J, Lv P, Ionics, 19, 221 (2013)
- Zhang HL, Liu SH, Li F, Bai S, Li C, Tan J, Cheng HM, Carbon, 44, 2212 (2006)
- Wan CY, Li H, Wu MC, Zhao CJ, J. Appl. Electrochem., 39(7), 1081 (2009)
- Yosio M, Wang H, Fukuda K, Umeno T, Abe T, Ogumi Z, J. Mater. Chem., 14, 1754 (2004)
- Dahn JR, Phys. Rev. B, 44, 9170 (1990)
- Gan L, Guo HJ, Wang ZX, Li XH, Peng WJ, Wang JX, Huang SL, Su MR, Electrochim. Acta, 104, 117 (2013)
- Wang HY, Yoshio M, J. Power Sources, 93(1-2), 123 (2001)
- Ma Z, Zhuang YC, Deng YM, Song XN, Zuo XX, Xiao X, Nan JM, J. Power Sources, 376, 91 (2018)
- Xie J, Tong L, Su LW, Xu YW, Wang LB, Wang YH, J. Power Sources, 342, 529 (2017)
- Aurbach D, Markovsky B, Weissman I, Levi E, Ein-Eli Y, Electrochim. Acta, 45(1-2), 67 (1999)
- Gaberscek M, Dominko R, Jamnik J, Electrochem. Commun., 9, 2778 (2007)