In the present work, an investigation on the susceptibility to hydrogen embrittlement of AISI 304 and 310 austenitic stainless steels was performed. The hydrogen embrittlement process leads to degradation of mechanical properties and can be accelerated by the presence of surface defects combined with elevated surface hardness. Tensile test specimens of the selected materials were machined by turning with different cutting parameters in order to create variations in surface finish conditions. The samples thus prepared were submitted to tensile tests before and after hydrogen permeation by cathodic charging. Regarding the AISI 304 steel, it was possible to notice that the presence of strain-induced martensite on the material surface led to severe hydrogen embrittlement. In the case of the AISI 310 steel, due to its higher nickel amount, no martensite formation could be detected, and this steel was found to be less susceptible to embrittlement in the tested conditions. (C) 2019 Hydrogen Energy Publications LLC. Published by Elsevier Ltd. All rights reserved.