Ceramic foams with significant porosity and robust mechanical properties have received extensive attentions. However, it is still difficult to achieve excellent compressive strength at high porosity levels. In this work, a gelation of foamed boehmite sol method is proposed to settle this issue. The technological parameters during preparation process are systematically investigated. As-prepared alumina ceramic foams possess unprecedentedly high compressive strength of 34.1-89.1MPa at high porosity levels of 66.0%-87.2%, which is attributed to the present of hierarchical pore structure, small grain size and pore size. This work demonstrates a facile and novel method for the fabrication of high-performance alumina ceramic foams toward practical applications.