The influence of the three nonionic surface active agents such as Tween 20, Tween 80, and Tetronic 90R4 on hydrolysis, setting reaction, microstructure, and mechanical properties of alpha tricalcium phosphate (alpha-TCP) based materials was determined. The study revealed that the addition of any of the surfactants mentioned above slightly prolonged the setting time of the tested cements (up to 5 min). On the other hand, it was found that surfactants influence the long-term hydrolysis reaction. The addition of surfactants also affected the microstructure of the final materials, especially after incubation in a simulated body fluid. Surface active agents also had an impact on mechanical behavior of the obtained cements. Sorbitan esters, Tween 20 and Tween 80, decreased compressive strength in comparison to the reference material (6.56 +/- 1.59 MPa) to 3.54 +/- 1.18 and 3.68 +/- 1.03 MPa, respectively. Interestingly, Tetronic 90R4, never used before as an additive to calcium phosphate bone cements (CPCs) caused a 2-fold increase of this value (up to 13.28 +/- 1.59 MPa). All the developed materials exhibited bioactivity in vitro. The obtained results shed new light on surfactants as CPCs additives. They should not only be considered as foaming agent or binders, but also they deserve more attention as modifiers affecting the physicochemical properties of alpha-TCP based materials.