Stable silicone fluid-carbon nanotube dispersions were prepared in minutes by simple mixing processes, without the addition of solvents or surfactants and without the chemical modification of the nanotubes. With linear silicones of sufficient viscosity, a dual asymmetric centrifuge (SpeedMixer) was sufficient for dispersion; lower viscosity silicones required a brief ultrasound treatment. Optical microscopy indicates a homogeneous dispersion of multiwalled carbon nanotube (MWCNT) bundles in linear poly(dimethylsiloxane) (PDMS) oils. The facile dispersion of carbon nanotubes in PDMS has been reported in several previous publications and this appears to be general for silicones. MWCNTs also disperse readily, and to a greater extent, as assessed by optical microscopy, in poly(methylphenylsiloxane) and, in particular, poly(diethylsiloxane). Linear PDMS/MWCNT dispersions are stable against agglomeration for months. Platinum-catalyzed hydrosilylation of MWCNT-containing vinyl-/hydride-functionalized PDMS liquids yielded filled elastomers that unexpectedly exhibit significantly increased thermal stability. This enhancement occurs with only fractions of a weight percent of MWCNTs. Thermal gravimetric analysis shows a 54 degrees C increase in peak weight loss temperature (446-500 degrees C), an increased decomposition activation energy (158-233 kJ/mol), a second higher temperature decomposition process, and doubled char formation (20-40%) with only 0.5 wt %-added MWCNT. Pyrolysis combustion flow calorimetry confirmed the enhancement in thermal stability. Improvements in electrical conductivity were observed at loadings as low as 0.025 wt %. Spontaneous adsorption of dialkylsiloxane chains to MWCNT surfaces (wetting) and the resulting changes in the composite structure are implicated as the basis for dispersion and thermal behavior changes.