Palladium membranes used for hydrogen separation seemingly develop cavities filled with hydrogen, i.e. hydrogen bubbles, along the grain boundaries. These bubbles may represent initial stages of pinhole formation that lead to unselective leakage and compromise the long-term stability of the membranes. Alloying with Ag improves the permeability of Pd, but whether these H-2 bubbles form in Pd-Ag membranes remained unknown. In this work, the microstructure of a Pd77Ag23 membrane was characterized by election microscopy after H-2 permeation testing for 50 days at 15 bar at temperatures up to 450 degrees C. The results show that Ag does not prevent bubbles from emerging along high-angle grain boundaries, but reduces the number of potential nucleation sites for cavity formation by supressing the development of dislocation networks when H-saturated Pd is cycled through the miscibility gap. Both magnetron-sputtered and electroless plated membranes are afflicted by H-2 bubbles, thus their formation seems determined by intrinsic properties of the material independent of the fabrication technique. The qualitative discussion enables to point directions for enhancement of membrane stability. (C) 2019 The Authors. Published by Elsevier Ltd on behalf of Hydrogen Energy Publications LLC.