In the present study, the hydrogen storage performance of multi-principal-component ZrTiVNiCrFe alloy produced through rapid solidification has been examined by electro-chemical methods and gas-solid reactions. XRD and EBSD analyses reveal the hexagonal Laves phase structure (type C14) with average grain size of 300 nm and root-mean-square microstrain of 0.19%. Cyclic voltammetry and electrochemical impedance spectroscopy analyses in the hydrogen sorption/desorption region give insight to the sorption/desorption kinetics and the change in the desorption charge in terms of the applied potential. The pressure-composition isotherms measured in course of gas-solid reaction confirm the hydrogen storage capacity reaching 1.6 wt% at the first hydrogenation at room temperature, then reducing to 1.3-1.4% during subsequent cycling. According to the calorimetric titration study, there is a significant hysteresis primarily caused by the non-equilibrium character of the hydrogenation process. (C) 2019 Hydrogen Energy Publications LLC. Published by Elsevier Ltd. All rights reserved.