For large scale application of fuel cells, low platinum loading electrode structures are necessary. An electrode based on a highly porous carbonized polyacrylonitrile foam material with very low platinum loading (similar to 13 mu g cm(-2)) was prepared. The performance of this electrode for oxygen reduction was evaluated and compared with bulk platinum and glassy carbon electrodes.