Low temperature catalysts are attracting increasing attention in the selective catalytic reduction (SCR) of NO with NH3. MnOx-decorated MgAl layered double oxide (Mn/MgAl-LDO) was synthesized via a facile fast pour assisted co-precipitation (FP-CP) process. Compared to the Mn/MgAl-LDO obtained via slow drop assisted co-precipitation (SD-CP) method, the Mn/MgAl-LDO (FP-CP) has excellent activity. The Mn/MgAl-LDO (FP-CP) catalyst was shown to possess a high NO conversion rate of 76%-100% from 25 to 150 degrees C, which is much better than the control Mn/MgAl-LDO (SD-CP) (29.4%-75.8%). In addition, the Mn/MgAl-LDO (FP-CP) offered an enhanced NO conversion rate of 97% and a N-2 selectivity of 97.3% at 100 degrees C; the NO conversion rate was 100% and the N-2 selectivity was 90% at 150 degrees C with a GHSV of 60,000 h(-1). The Mn/MgAl-LDO (FP-CP) catalyst exhibited a smaller fragment nano-sheet structure (sheet thickness of 7.23 nm). An apparent lattice disorder was observed in the HRTEM image confirming the presence of many defects. The H-2-TPR curves show that the Mn/MgAl-LDO (FP-CP) catalyst has abundant reducing substances. Furthermore, the enhanced surface acidity makes the NH3 concentration of the Mn/MgAl-LDO (FP-CP) catalyst lower than 100 ml.m(-3) after the reaction from 25 to 400 degrees C. This can effectively reduce the ammonia escape rate in the SCR reaction. Thus, the Mn/MgAl-LDO (FP-CP) catalyst has potential applications in stationary industrial installations for environmentally friendly ultra-low temperature SCR. (C) 2020 The Chemical Industry and Engineering Society of China, and Chemical Industry Press Co.. Ltd. All rights reserved.