The surface of poly (p-phenylene benzobisoxazole) (PBO) fibers with self-healing and ultraviolet (UV) resistance performance play the key role in prolonging their service lifespan. Although great advances have been made in the single aspect of above two properties, integration of self-healing and anti-UV performance into the surface of PBO fiber is still a challenge. In this study, the coagulation strategy mediated by metal-organic framework (MOF) is proposed to construct the multifunctional surface of PBO fibers. The spindle-like iron (III)-based MOF (MIL-88B-NH2) nanocrystals are firstly immobilized onto the surface of PBO-COOH through hydrothermal reaction, then serving as the medium layer to further immobilize sufficient graphene oxide (GO) nanosheets. Benefitting from the favorable near-infrared (NIR, 808 nm) photothermal conversion performance of GO nanolayers, the monofilament compositePBO@Fe-MIL-88B-NH2-GO-TPU (thermoplastic polyurethane) exhibited a stable and high self-healing efficiency (approximately 80%) within five cycle times. Meanwhile, the cooperative adsorption and shielding weaken effects of MOF-GO nanolayers enabled PBO fibers with excellent anti-UV properties that are superior to much reported literatures after 96 h aging time and eventually increased by 75% compared with untreated PBO fiber. In view of the varieties and multifunctionalities of MOFs and carbon nanomaterials, MOF-mediated coagulation strategy would provide guidance for preparing multifunctional composite materials. (c) 2020 Elsevier Inc. All rights reserved.