Cellulose nanocrystals (CNCs) were converted into a CO2-responsive composite nanomaterial by grafting poly(dimethylaminoethyl methacrylate) (PDMAEMA), poly(diethylaminoethyl methacrylate) (PDEAEMA), and poly(diisopropylaminoethyl methacrylate) (PDPAEMA) onto its surface using both grafting-to and grafting-from approaches. The zeta potential (zeta) of the graft-modified CNC could be reversibly switched by protonation/deprotonation of the tertiary amine groups simply by sparging with CO2 and N-2, respectively. Depending on the grafting density and the molecular weight of the polymer grafts, CNC can form stable aqueous dispersions at either mildly acidic pH (under CO2) or mildly basic (under N-2) conditions. Moreover, it was also determined that the CNC hydrophobicity, assessed using phase-shuttling experiments at different pH values, was also dependent on both the grafting density and molecular weight of the polymer grafts, thereby making it possible to easily tune CNC dispersibility and/or hydrophobicity.