We report scanning tunneling microscopy results obtained on nominally (110) oriented, slightly miscut Au and Ag surfaces studied in ultrahigh vacuum at ambient and low temperatures (50 K). On these surfaces extended areas comprised of vicinal planes were observed and they exhibit intriguing step structures. An analysis of these planes in terms of their orientation, atomic structures, and steps is presented.