The oxalate-bridged complex {NPr4[MnCr(ox)(3)]}(x) (1) was prepared and its magnetic properties were studied, where NPr4+ = tetra(n-propyl)ammonium ion, ox(2-) = oxalate ion. X-ray powder pattern measurements suggested that the distance between the layers consisting of alternate array of Mn2+ and Cr3+ through ox(2-) ligands is shorter in 1 than {NBu(4)[MnCr(ox)(3)]}(x) (2) (NBu(4)(+) = tetra(n-butyl)ammonium ion). The magnetic transition temperature of 1 (T-c = 6.3+/-0.2 K) determined from ac magnetic measurements was, however, almost the same as the T-c reported for 2. In contrast with the case of 2, compound 1 showed a normal magnetization curve which saturates rapidly with the increase of magnetic field (below 10 kG).