The bulk free radical copolymerizations of 2-hydroxyethyl methacrylate (HEMA) with n-butyl methacrylate (BMA) or cyclohexyl methacrylate (CHMA) were studied over the composition mole fraction interval of 0-1 for HEMA in the monomer feed. The C-13 NMR (125 MHz) spectra of the copolymers were analysed to determine the copolymer composition and the stereochemical configuration of the copolymers. The terminal model reactivity ratios of HEMA and BMA were found to be r(HEMA) = 1.73 and r(BMA) = 0.65 and for HEMA and CHMA, r(HEMA) = 1.26 and r(CHMA) = 0.31. The BMA and CHMA homopolymers were found to be predominantly syndiotactic with isotacticity parameters of theta(BB) = 0.18 and theta(CC) = 0.19, respectively. The copolymers were also found to be predominantly syndiotactic, indicating a strong tendency for racemic additions of the monomers in the formation of the copolymers. The diffusion of water into cylinders of poly(HEMA-co-BMA) and poly(HEMA-co-CHMA) was studied over a range of copolymer compositions and was found to be Fickian. The diffusion coefficients of water at 37 degrees C were determined from swelling measurements and were found to vary from 1.72 x 10(-11) m(2) s(-1) for polyHEMA to 0.97 x 10(-11) m(2) s(-1) for poly(HEMA-co-BMA) having a mole fraction F-HEMA = 0.80 and to 0.91 x 10(-11) m(2) s(-1) for a poly(HEMA-co-CHMA) also having F-HEMA = 0.80. The mass of water absorbed at equilibrium relative to the mass of dry polymer varied from 58.8 for polyHEMA to 27.2% for poly(HEMA-co-BMA) having F-HEMA = 0.85 and to 21.3% for poly(HEMA-co-CHMA) having F-HEMA = 0.80.