Epoxy resins and other thermosetting polymers change from liquids to solids during cure. A precise process model of these materials requires a constitutive model that is able to describe this transformation in its entirety. In this st1udy the viscoelastic properties of a commercial epoxy resin were characterized using a dynamic mechanical analyzer (DMA). Specimens were tested at several different cure states to develop master curves of stress relaxation behavior during cure. Using this experimental data, the relaxation modulus was then modeled in a thermorheologically complex manner. A Prony (exponential) series was used to describe the relaxation modulus. An original model was developed for the stress relaxation times based on similar work by Scherer (16) on the relaxation of glass. Shift functions used to obtain reduced times are empirically derived based on curve fits to the data. The data show that the cure state has a profound effect on the stress relaxation of epoxy. More important, the relaxation behavior above gelation is shown to be quite sensitive to degree of cure.