The linear viscoelastic behavior of a soda-lime-silica glass under low frequency shear loading is investigated in the glass transition range. Using the time-temperature superposition technique, the master curves of the shear dynamic relaxation moduli are obtained at a reference temperature of 566 degrees C. A method to determine the viscoelastic constants from dynamic relaxation moduli is proposed. However, some viscoelastic constants cannot be directly measured from the experimental curves and others cannot be precisely obtained due to non-linearity effects at very low frequencies. The generalized Maxwell model is investigated from the experimental dynamic moduli without fixing the viscoelastic constants. A set of parameters is shown to be in good agreement with the experimental dynamic relaxation moduli, but does not give the correct values of the viscoelastic constants of the investigated glass. The soda-lime-silica glass exhibits a non-linear viscoelastic behavior at very low stress level which is usually observed for organic glasses. This non-linear behavior is questioned.