Several dense polyamide-6 membranes were prepared by casting 7 wt% and/or 10 wt% solutions of polymer in trifluoroethanol. The cast membranes were dried at different temperatures from 25 to 80 degrees C. Sorption and pervaporation properties of PA-6 membranes in water-ethanol mixtures were obtained. The data obtained showed that water was preferentially sorbed into the membrane and transported through the membrane; however, the pervaporation selectivity factor alpha(PV) was dose to unity at higher concentrations, The selectivity parameters in pervaporation were improved for membranes obtained from 10 wt% polymer and dried at higher temperatures.