This paper investigates the effects of the diphasic structure on the optoelectronic properties of hydrogenated microcrystalline silicon (mu c-Si:H) films prepared in a triode three-chamber plasma-enhanced chemical vapor deposition (PECVD) system. The influences of boron-compensation doping on the dark-and photo-conductivity of mu c-Si:H films are also described. A tandem solar cell with an entirely mu c-Si:H p-i-n bottom cell and an a-Si:H top cell has been prepared with an initial conversion efficiency of 8.91% (0.126 cm(2), AM1.5, 100 mW/cm(2)).