Solid State Ionics, Vol.76, No.1-2, 35-39, 1995
Gamma-Radiation Induced Cross-Linked Peo-Liclo4 Solid-Electrolyte System
Aimed at raising the room temperature ionic conductivity of PEO-based solid polymer electrolyte and considered that the ionic conduction preferentially occurs in the amorphous phase, we lightly crosslinked the high MW PEO through gamma-irradiation and further suppressed the residual crystallinity by plasticizing with propylene carbonate. By incorporating LiClO4 salt to the above described polymer host, the ambient (25 degrees C) ionic conductivity of the electrolyte system could reach as high as 6.8 X 10(-4) S/cm. As the electrolyte was a crosslinked system, it was mechanically self-supportable. Based on the preliminary results of the electrochemical performance of the secondary lithium battery, assembled by using this kind of solid electrolyte and polyaniline as positive electrode, it is realized that the electrolyte thus prepared is of high expectancy.