The 2D Rancieite type manganic acid was prepared by reduction of KMnO4 in acidic medium. Its ion exchange behavior allows to prepare alkali derivatives. All compounds were characterized with use of a combination of X-ray diffraction, chemical analyses, TGA, magnetic measurements and spectroscopic techniques. The evolution of their chemical composition versus temperature was studied between 180 and 400 degrees C. It shows that the dehydration process is partly reversible in these compounds whereas the weak reduction is irreversible. The 2D Rancieite-type manganic acid is readily different from a Birnessite-type phyllomanganate, as shown by several features : the interlayer distance, the ion exchange capacity, the thermal behavior, the interlayer cation content, the manganese average oxidation state, the magnetic behavior and the IR spectrum.