Stretching a stacked sPP lamellar morphology at room temperature leads to a mechanical induced transformation from the (t(2)g(2))(2) (helical) into the (tttt) (zigzag) chain conformation of the polymer. The so prepared samples exhibit after annealing above 80 degreesC a thermal induced retransformation into the cell I and cell III crystal structure of the helical chain conformation. The mechanical induced chain conformational transformation as well as the thermal induced retransformation was studied by means of transmission electron microscopy and electron diffraction.