Femtosecond infrared spectroscopy was used to study the electron injection dynamics of Re(CO)(3)Cl(dcbpy) (ReCOA) and related derivatives on the surface of TiO2 nanocrystalline thin films. We prepared two derivatives of ReCOA by inserting 1 and 3 CH2 spacers (ReC1A and ReC3A respectively) between the bipyridine rings and the carboxylate anchoring groups. We directly observed electron injection from the excited states of Re dyes to TiO2 by simultaneously measuring the broad absorption of injected electrons and the vibrational spectrum of the complex in its ground, excited, and oxidized states. Electron injection from ReCOA to TiO2 was found to occur on the <100-fs time scale, whereas the excited state vibrational spectrum evolved with a time constant of a few picoseconds, indicating that injection occurred before complete vibrational relaxation in this system. We found that the electron injection rate decreased by a factor of >200 from ReCOA to ReC1A. This decrease is much larger than the predicted change for nonadiabatic electron transfer (ET) processes, in which ET rate depends exponentially on the length of CH2 spacers. This result as well as ultrafast injection rate indicate an adiabatic electron injection process in ReCOA-sensitized TiO2. In contrast, the electron injection rate decreased by a factor of 13.7 from ReC1A to ReC3A, which agrees qualitatively with the trend predicted for nonadiabatic ET processes.