Dense sodium alginate (SA) membranes crosslinked with glutaraldehyde (GA) have been prepared by the solution method, wherein a nonsolvent of SA (acetone) was used in a reaction solution instead of an aqueous salt solution. Through infrared radation, X-ray diffractometry, and the swelling measurement, the crosslinking reaction between the hydroxyl groups of SA and the aldehyde groups of GA was characterized. To investigate the selective sorption behavior of the crosslinked SA membranes, swelling measurements of the membranes in ethanol-water mixtures of 70-90 wt % ethanol contents were conducted by equipment that was able to measure precisely the concentration and amount of the liquid absorbed in the membranes. It was observed that the crosslinking could reduce both the solubility of water in the resulting membrane and the permselectivity of the membrane toward water at the expense of membrane stability against water. The pervaporation separation of a ethanol-water mixture was conducted with the membranes prepared at different GA contents in the reaction solution. When the membrane was prepared at a higher GA content, both flux and separation factor to water were found to be reduced, thus resulting from the more crosslinking structure in it. The pervaporation separations of ethanol-water mixtures were also performed at different feed compositions and temperatures ranging from 40 to 80