Based on the character of a clay that could be separated into many 1-nm thickness monolayers, clay styrene-butadiene rubber (SBR) nanocomposites were acquired by mixing the SBR latex with a clay/water dispersion and coagulating the mixture. The structure of the dispersion of clay in the SBR was studied through TEM. The mechanical properties of clay/SBR nanocomposites with different filling amounts of clay were studied. The results showed that the main structure of the dispersion of clay in the SBR was a layer bundle whose thickness was 4-10 nm and its aggregation formed by several or many layer bundles. Compared with the other filler, some mechanical properties of clay/SBR nanocomposites exceeded those of carbon black/SBR composites and they were higher than those of clay/SBR composites produced by directly mixing clay with SBR through regular rubber processing means.