The preparation of poly(DL-lactide-co-glycolide) (PLGA) nanoparticles was performed by a dialysis method without surfactant or emulsifiers. The size of the PLGA nanoparticles prepared from dimethylacetamide (DMAc) as an initial solvent was smaller than that from acetone. The sizes of the PLGA nanoparticles from DMAc and acetone were 200.4 +/- 133.0 and 642.3 +/- 131.1 nm, respectively. The effects of the initial solvent selected to dissolve the copolymer and the lactide:glycolide ratio were investigated. The PLGA nanoparticles were spherical as revealed by the results of scanning electron microscopy and transmission electron microscopy observations. From these results it was shown that PLGA nanoparticles could be formed by the dialysis method without surfactant. The drug-loading contents and efficiency were also dependent on the lactide:glycolide ratio and initial feeding amount of the drug. A higher lactide ratio resulted in higher drug loading and higher loading efficiency. However, a higher initial feeding amount of the drug resulted in higher drug loading and lower loading efficiency. Clonazepam was released for at least 2 days and the release rate was slower with a higher lactide:glycolide ratio and a larger amount of drug-loading nanoparticles than that with a lower lactide:glycolide ratio and a smaller amount of drug-loading nanoparticles.