Nylon 10 10 crystals, which isothermally crystallized from the molten state and cold crystallized from melt-quenched samples at various temperatures, were investigated by using temperature-variable wide angle X-ray diffraction (WAXD) and small angle X-ray scattering (SAXS). No Brill transition occurred for the melt-crystallized crystals. However, this transition was easily observed for the cold-crystallized nylon 10 10, and the transition temperature is pertinent to the crystallization temperature. The sizes of these crystals was determined by SAYS and correlated with the Brill transition temperatures (T-B). It was found that the T-B had a linear relationship with the size of crystals, which was used to predict the T-B for those crystals with thick lamella and to calculate the crystal size showing T-B below room temperature. Nylon 10 10 crystal will possess the gamma form (pseudohexagonal form) rather than the a phase at room temperature if its size becomes small enough.