Through elucidating the effects of current density, cupric ion concentration, bath temperature, and air agitation on plating uniformity and filling capability of copper electroplating, the deposition of copper in an acid copper electrolyte will be illustrated to scale down to the sub-0.13 mum features with uniform plating, which is required by chemical mechanical polishing in current damascene techniques. In order to achieve the defect-free filling in sub-0.13 mum vias and trenches, the electrolyte must be composed of proper amounts of cupric ions, sulfuric acid, chloride ions, wetting agent, and filling promoter. The supplied current controlled at a lower current density, agitation acceded to the electroplating process were found as further keys. In the electrolyte, the filling promoter was consisted essentially of thiazole derivatives with benzyl groups and amino-group (-NH2) offering sufficient inhibition on copper depositing and selective inhibition gradient. Moreover, a lower resistivity film and higher filling capability could be obtained by using periodic pulse current plating as compared with direct current plating.