The structural changes which occur on the gamma -radiolysis of poly(dimethyl siloxane) (PDMS) under vacuum at 303 K have been investigated using Si-29 and C-13 NMR. New structural units consistent with main chain scission and crosslinking through both H-linking and Y-linking reactions have been identified. The results obtained at various absorbed doses have been used to calculate the G-values for scission and crosslinking. G-values for scission of G(S) = 1.3 +/- 0.2, for H-linking of G(D-CH2-R) = 0.34 +/- 0.02 and for Y-Linking of G(Y) = 1.70 +/-0.09 were obtained for radiolysis under vacuum at 303 K. Thus crosslinking predominates over scission for radiolysis of PDMS under these conditions, and, by contrast with previous studies, Y-links have been shown to be the predominant form of crosslinks.