We synthesized six water-soluble polymeric complexes of sorbic acid with poly vinylpyrrolidone of different molecular weight (mol wt). As shown by infrared absorption spectrum analysis, the complexes were formed by hydrogen bonding. The complexes (SC I, with mol wt=10 kDa, SC2 with mol wt=25 kDa, SO with mol wt=30 kDa, SC4 with mol wt=40 kDa, SC5 with mol wt=90 kDa, and SC6 with mol wt=360 kDa) were characterized as low mol wt (SCI, SC2, and SC3) and high mol wt (SC4, SC5, and SC6). The antifungal potencies of the complexes were tested by the macrodilution susceptibility method against environmental and clinically important fungi. Sorbic acid as well as the complexes exhibited minimum inhibitory concentrations (MICs) lower than potassium sorbate against all the strains tested. MICs of SC1, SC2, and SC3 were shown to be 2- to 4-fold lower for yeast and 1.5- to 3-fold lower than those of sorbic acid for moulds, respectively. The MICs of SC4 and SC5 against both of the Candida species tested ranged from 500 to 800 mug/ml, whereas for SC6 and sorbic acid they were about I mg/ml. The potencies of the high mol wt complexes against moulds were decreased by increasing the mol wt. For both of the moulds tested, the MICs of SC4 were slightly lower than those of sorbate. The MICs of sorbic acid and SC5 were equal to 300 mug/ml and 500 mug/ml respectively for Aspergillus parasiticus and for Penicillum viridicatum. The susceptibility to SC6 of all of the hyphomycetes tested was higher than that to sorbic acid. The low mol wt complexes and the sorbic acid exhibited minimal fungicidal concentrations (MFCs) 2 and 3 times higher respectively than the MICs. Sorbic acid and SC3 at a concentration of 2.5 mg/ml in an in vitro time kill curve study of Candida tropicalis were shown to be fungistatic, whereas SCI and SC2 were fungicidal at the same concentrations. For Aspergillus parasiticus sorbic acid at 2.5 mg/ml was fungistatic for a 24-h period, whereas SC1, SC2, and SC3 were fungicidal.