The porous oxide layer obtained by phosphoric anodic oxidation (PAO) of 1050 and 2024T3 aluminium alloys is modified by impregnation with zinc under alternating voltage. The resulting current against applied voltage relationship shows that a threshold voltage is required to deposit the zinc. Beyond a low critical voltage, V-cL, zinc electrocrystallization starts near the barrier layer and grows with time through the porous oxide layer whatever the alloy used as substrate. For the 2024T3 alloy, beyond a high critical voltage V-cH, S.I.M.S. analysis shows that zinc is also present on top of the oxide layer. The distribution of zinc particles depends on the porous layer morphology: formation of zinc needles in a columnar form (1050 alloy) and dispersion of zinc particles in a disorganized structure (2024T3 alloy). The polarization curves obtained in a 3 wt % NaCl solution show a decrease in anodic and cathodic currents indicating a protective effect of zinc impregnation, confirmed by electrochemical impedance analysis.