The graft copolymer of high impact polystyrene (HIPS) grafted with malice anhydride (MA) (HIPS-g-MA) was prepared with melt mixing in the presence of a free-radical initiator. The grafting reaction was confirmed by IR analyses and the amount of MA grafted on HIPS was evaluated by a titration method. 1-5 wt% of MA can be grafted on HIPS. HIPS-g-MA is miscible with HIPS. Its anhydride group can react with the PA6 during melt mixing the two components. The compatibility of HIPS-g-MA in the HIPS/PA6 blends was evident. Evidence of reactions in the blends was confirmed in the morphology and mechanical properties of the blends. A significant reduction in domain size was observed because of the compatibilization of HIPS-g-MA in the blends of HIPS and PA6. The tensile mechanical properties of the prepared blends were investigated and the fracture surfaces of the blends were examined by means of the scanning electron microscope (SEM). The improved adhesion in a 16%HIPS/75%PA6 blend with 9%HIPS-g-MA copolymer was detected. The morphology of fibrillar ligaments formed by PA6 connecting HIPS particles was observed.