Electrochemical investigations on low-Si alloyed steels with Si content ranging from 0.25 to 3.2 wt.% were carried out in a 0.1 M NaCl borate-buffered solution (pH 8.4) in reducing conditions at 90 degreesC. Silicon as an alloying element was proved to degrade at first the steel ability to passivate. For longer immersion times, protective effects developed more efficiently on the steel containing 3.2 wt.% silicon. Passive layers electrochemically formed in the transpassive domain on the steel containing 3.2% Si were shown to be significantly different from those grown at rest potential.