An interpenetrating polymer network (IPN) hydrogel composed of chitosan and polyallylamine exhibited electric-sensitive behavior. The chitosan/polyallylamine IPN hydrogel was synthesized by radical polymerization using 2,2-dimethoxy-2-phenylacetophenone (DMPAP) and methylene bisacrylicamide (MBAAm) as initiator and crosslinker, respectively. The swelling behavior of the IPN was studied by immersion of the gel samples in aqueous NaCl solutions at various concentrations and pHs. The swelling ratio decreased with increasing concentration and pH of electrolyte solution. The stimuli response of the IPN hydrogel in electric fields was also investigated. When a swollen the IPN was placed between a pair of electrodes, the IPN exhibited bending behavior in response to the applied electric field. The IPN also showed stepwise bending behavior depending on the electric stimulus. In addition, thermal properties of the IPN were investigated by differential scanning calorimetry (DSC) and dielectric analysis (DEA).