The present work reports evolution of morphology from initial (presence of striation) to final (droplet formation) stages in a single-screw extruder. Morphology development during the blending process controls the final size of the dispersed phase, which in turn significantly affects the properties of the blends. The experiments were carried out using a 70/30 wt% polypropylene/ethylene vinyl acetate (PP/EVA) blend; samples were collected along the length of the screw, by screw pullout experiment, to analyze the size and size distribution of the dispersed phase present both as striated layers and subsequently as droplets. Average size of the dispersed phase and standard deviation were taken into account to monitor the morphology evolution along the length of the screw. Pre-breakup morphology development was studied by analyzing the sample collected from the feed zone of the extruder in terms of upper and lower layers along the cross section of screw channel. Examination of micrographs revealed the existence of pattern of ordered striations along the length of the melting zone containing striations from average size of 1000 mum down to 50 mum decreasing rapidly along the length of the screw. The breakup process was captured at the start of compression zone where step-up in the shear as well as elongational flow was applied due to decrease in the channel depth along the compression zone. The observed droplet size formed by the breakup of filaments is found to be in accordance with theory. The final droplet size is found to be governed by the emulsification process occurring as a result of stretching, breakup and coalescence in the metering section of the screw and is in the order of 2 mum.