This study was aimed at understanding how the process conditions affect the weld-line strength and microstructure of injection molded microcellular parts. A design of experiments (DOE) was performed and polycarbonate tensile test specimens were produced for tensile tests and microscopic analysis. Injection molding trials were performed by systematically adjusting four process parameters (i.e., melt temperature, shot size, supercritical fluid (SCF) level, and injection speed). For comparison, conventional solid specimens were also produced. The tensile strength was measured at the weld line and away from the weld line. The weld-line strength of injection molded microcellular parts was lower than that of its solid counterparts. It increased with increasing shot size, melt temperature, and injection speed, and was weakly dependent on the supercritical fluid level. The microstructure of the molded specimens at various cross sections were examined using scanning electron microscope (SEM) and a light microscope to study the variation of cell size and density with different process conditions.