Pitting corrosion of stainless steels causes tremendous damage in terms of material loss and resulting accidents. Organic surfactants have been tried as pitting inhibitors but the understanding of the inhibition mechanisms is mainly speculative. In the present study the inhibition of the pitting corrosion of 304 stainless steel by N-lauroylsarcosine sodium salt (NLS) in 0.1 M NaCl solutions at neutral pH was studied using an approach that combines surface chemical techniques with electrochemical ones. It was found that NLS increases the pitting resistance of 304 stainless steel, with possible complete inhibition at high NLS concentration (30 mM). Adsorption of NLS on 304 stainless steel particles was directly measured. NLS adsorbs significantly on 304 stainless steel with maximum adsorption density close to bilayer coverage. Electrophoretic mobility data for 304 stainless steel particles show that the surface of 304 stainless steel is negative in NaCl solution at neutral pH. The adsorption of NLS makes the interfacial charge even more negative. The relationship between pitting inhibition and adsorption density of NLS suggests that NLS does not adsorb preferentially on the pit nucleation sites and complete inhibition requires that the whole surface be covered completely by NLS. The inhibition mechanism of NLS is proposed to be due mainly to the blocking effect of a negatively charged NLS adsorption layer. This study shows that in addition to the adsorption amount of surfactant, interfacial charge also plays an important role in pitting inhibition. (C) 2003 Elsevier Science (USA). All rights reserved.