An interpenetrating polymer network (IPN) composed of poly(vinyl alcohol) (PVA) and poly(N-isopropylacrylamide) (PNIPAAm) was prepared by the sequential IPN method. The equilibrium swelling ratio and bending behavior under electric fields of the IPN hydrogel were measured in an aqueous NaCl solution. The IPN exhibited a high equilibrium swelling ratio, in the range 280-380%. When the IPN in aqueous NaCl solution was subjected to an electric field, the IPN showed significant and quick bending toward the cathode. The IPN hydrogel also showed stepwise bending behavior, depending on the electric stimulus. In addition, the ionic conductivity of the IPN hydrogel was measured using dielectric analysis, and its conductive behavior followed the Arrhenius equation. The conductivity of the IPN hydrogel and the activation energy for the form of the IPN were 1.68 x 10(-5) S/cm at 36degreesC and 61.0 kJ/mol, respectively. (C) 2003 Wiley Periodicals, Inc.