Graft copolymers of acrylamide on cellulose materials (a-cellulose 55.8%, DP 287.3) obtained from Terminalia superba wood meal and its carboxymethylated derivative (DS 0.438) were prepared using a ceric ion initiator and batch polymerization and modified batch polymerization processes. The extent of graft polymer formation was measured in graft level, grafting efficiency, molecular weight of grafted polymer chains, frequency of grafting as a function of the polymerization medium, and initiator and monomer concentrations. It was found that the modified batch polymerization process yielded greater graft polymer formation and that graft copolymerization in aqueous alcohol medium resulted in enhanced levels of grafting and formation of many short grafted polymer chains. Viscosity measurements in aqueous solutions of carboxymethyl cellulose-g-polyacrylamide copolymer samples showed that interpositioning of polyacrylamide chains markedly increased the specific viscosity and resistance to biodegradation of the graft copolymers. The flocculation characteristics of the graft copolymers were determined with kaolin suspension. (C) 2003 Wiley Periodicals, Inc.