The kinetics of the thermal degradation and thermal stability of conductive silicone rubber filled with conductive carbon black was investigated by thermogravimetric analysis in a flowing nitrogen atmosphere at a heating rate of 5degreesC/min. The rate parameters were evaluated by the method of Freeman-Carroll. The results show that the thermal degradation of conductive silicone rubber begins at about 350degreesC and ends at about 600degreesC. The thermal degradation is multistage, in which zero-order reactions are principal. The kinetics of the thermal degradation of conductive silicone rubber has relevance to its loading of conductive carbon black. The activation energies are temperature-sensitive and their sensitivity to temperature becomes weak as temperature increases. In addition, the conductive silicone rubber filled with conductive carbon black has better thermal stability than that of silicone rubber without any fillers. Also, conductive silicone rubber filled with conductive carbon black has better thermal stability than that of silicone rubber filled with the same amount of silica. (C) 2003 Wiley Periodicals, Inc.