Aromatic poly(ether-ketone)s having pendant carboxyl groups have been obtained by direct, one-pot, Friedel-Crafts copolycondensation of 4,4'-diphenoxybenzophenone with a mixture of terephthaloyl chloride (TC) and trimellitic anhydride acid chloride (TAAC), over a wide range of TAAC/TC molar ratios, in the presence of anhydrous aluminum chloride. The syntheses were performed as precipitation-polycondensations, and the polymers were obtained in particulate form. Besides globular particles of polymer, small quantities of elongated, needlelike particles were observed when the mole ratio TAAC/TC was less than 1. Use of X-ray microdiffraction with synchrotron radiation has revealed that the needlelike material consists of a cyclic compound containing 10 phenylene units, i.e., the crystals are of a [2 + 2] macrocyclic dimer. The polymers obtained are soluble in strong acids and in mixtures of methanesulfonic acid or trifluoroacetic acid with chlorinated hydrocarbons. The molecular structures of the polymers were confirmed by H-1 and C-13 NMR spectroscopy. Reaction of TAAC with 4,4'-diphenoxybenzophenone produced mainly meta-orientation of the resulting ketone linkages. The size of the polymer particles, their molecular weights, and the melting behavior of the products obtained depend on the TAAC/TC ratio used. Ortho-keto acid residues, formed during reaction of anhydride groups of TAAC with 4,4'-diphenoxybenzophenone, exhibit ring-chain tautomerism. A carboxyl-containing aromatic polyketone derived from p-terphenyl, and thus having with no ether linkages in the main chain, was prepared by analogous chemistry, and functional derivatives of carboxy-substituted polyketones were also obtained and characterized.