Two new silver-antimony sulfides, [C2H9N2][Ag2SbS3] (1) and [C2H9N2](2)[Ag5Sb3S8] (2), have been prepared solvothermally in the presence of ethylenediamine and characterized by single-crystal X-ray diffraction, thermogravimetry, and elemental analysis. Compound 1 crystallizes in the space group Pn (a = 6.1781(1) Angstrom, b =11.9491(3) Angstrom, c = 6.9239(2) Angstrom, =111.164(1)degrees) and 2 in the space group Pm (a = 6.2215(2) Angstrom, b = 15.7707(7) Angstrom, c = 11.6478(5) Angstrom, beta = 92.645(2)degrees). The structure of 1 consists of chains of fused five-membered Ag2SbS2 rings linked to form layers, between which the template molecules reside. Compound 2 contains honeycomb-like sheets of fused silver-antimony-sulfide six-membered rings linked to form double layers. The idealized structure can be considered to be an ordered defect derivative of that of lithium bismuthide, Li3Bi, and represents a new solid-state structure type.