Solid-state dye-sensitized photovoltaic cells have been fabricated with TiO2 as the electron conductor and CuSCN as the hole conductor. These cells involve the nanoscale mixing of crystalline n-type and p-type semiconductors in films that. are more than 100 times thicker than the individual n- and p-type domains. Charge transport and field distribution in this kind of material are as yet unexplored. We have used photocurrent and photovoltage transients, combined with variation in the layer thickness, to examine the limiting factors in charge transport and recombination. Charge transport (t(1/2) approximate to 200 mus) is found to be similar to that in dye-sensitized electrolyte cells. Recombination at V-oc (t(1/2) approximate to 150 mus) is 10 times faster than in electrolyte cells, and recombination at short circuit (t(1/2) approximate to 450 mus) is 100 times faster. In the solid-state cells, the similarity of the charge transport and recombination rates results in a low fill factor, and photocurrent losses, both important limiting factors of the efficiency. A simple model is given, and suggestions are made for improvements in efficiency.