Monoshaped and monosized copper nanostructured particles have been prepared by potentiostatic electrochemical deposition on an ultrathin polypyrrole (PPY) film, electrochemically grown on a Si(100) substrate sputter-coated with a thin gold film or gold-film electrode (GFE). The crystal size and the number density of the copper nanocrystals have been examined by varying several deposition parameters, including the thickness of the gold film, the PPY film thickness, the applied potential, and the Cu2+ and the electrolyte concentrations for copper deposition. Optimal conditions for uniform growth of nanocrystals well-dispersed on the GFE have been determined, along with insight into the mechanism of crystal growth. A minimum gold film thickness of 80 nm is required to eliminate the effects of the gold-silicon interface. The PPY film thickness and homogeneity principally affect the shape uniformity of the nanocrystals, while the copper deposition potential could be used to regulate the size and number density of the nanocrystals. Both the Cu2+ and electrolyte concentrations are also found to play important roles in controlling the electrodeposition of nanocrystal growth.