We introduce a novel method for fabricating breath figure patterns on a homopolymer film by spin coating of polymer solutions with various solvents. The homopolymers employed in this study were cellulose acetate butyrate, monocarboxylated end-functional polystyrene, and poly(methyl methacrylate). Breath figure patterns were generated even when a water-miscible solvent such as tetrahydrofuran (THF) was used as a solvent. We even succeeded in generating breath figure patterns by spin coating even under a dry environment (relative humidity less than 30%), when water was directly added into THF solution. With the combination of the spin coating method, pores with a few hundred nanometers to several micrometers have been generated. We found that the pore size becomes larger with increasing water content in THF solution and decreasing rotating speed. This is equivalent to increasing humidity and decreasing evaporation speed, respectively, in the conventional method, which is direct solvent evaporation under a humid environment. Thus, compared with the conventional method for making breath figure patterns, this method would be very convenient for fabricating large-scale films with various pore sizes.