Copper concentrate (chalcopyrite) was granulated in a rotating drum with a diameter of 0.3 m and a length of 0.2 m. Water was used as the binder and it was sprayed onto the powder bed with a nozzle, This material exhibited induction type behaviour, which was defined by Iveson and Litster [AIChE J. 44 (1998) 1510]. Induction type behaviour is characterized by the occurrence of an induction stage, during which the granules are gradually being compacted and little or no growth occurs. At the end of this induction stage, binder liquid is squeezed from the interior of the granules onto the granule surface and the granules are then surface-wet. This results in a rapid growth rate of the granules. Different types of experiments were conducted. The influence of the nozzle pressure and the distance from the nozzle to the powder bed on the growth behaviour of the granules as well as on the binder distribution was examined. The results of these experiments led to the postulation of a modified mechanism for induction type behaviour: it was found that after the binder was delivered, there were large granules containing a high amount of binder and small granules containing less binder. During the induction stage, the granules are compacted and binder liquid continuously appears at the surface of the large granules. These wet spots that are continuously being formed pick up the dry and small granules. When all the small granules have been picked up, further expulsion of binder liquid onto the granules' surface results in granules that remain surface-wet. This phenomenon marks the end of the induction stage and it coincides with the disappearance of the small granules. The hypothesis was tested by selectively removing the smaller granules during an experiment. As expected, this resulted in a shorter induction time.