A liquid-crystalline epoxy resin was cured at two different temperatures. The phases of the cured systems clearly showed isotropic and nematic polydomain structures, which depended on the curing temperature. The fracture toughness of the systems was measured, and the fracture mechanism was investigated with polarized IR measurements. The nematic polydomain structure system showed considerably higher fracture toughness than the isotropic structure. Moreover, both systems exhibited a reorientation of the network chains near the fracture surface during the fracture process, and the region of the network reorientation in the nematic polydomain structure system was larger than that in the isotropic structure system. (C) 2004 Wiley Periodicals, Inc.