We demonstrated that the photopatterned single-layer adsorption film of poly(1-dodecyl-4-pyridinium bromide) on a silica surface was available for a template of nickel-phosphorus (Ni-P) electroless plating through sensitization with a SnCl2 aqueous solution and activation with a PdCl2 aqueous solution. Four kinds of poly(l-alkyl-4-vinylpyridinium halide)s bearing methyl, propyl, hexyl, and dodecyl groups were prepared. The cationic polymers were adsorbed by a negatively charged silica surface from their solutions, to form single-layer adsorption films exhibiting desorption-resistance toward deionized water and ethanol. The organic adsorption films could be decomposed completely by exposure to 172 nm deep-UV light. The formation and decomposition of the single-layer films were confirmed by deep-UV absorption spectral measurement and zeta-potential measurement. Ni-P electroless plating was carried out on the photopatterned adsorption films, using three types of SnOx colloidal materials without and with cationic or anionic surfactant as catalyst precursors in the sensitization step. In the case of the negatively charged SnOx colloids surrounded by anionic surfactant, Ni-deposition took place preferentially on the cationic adsorption films remaining in unexposed regions. The Ni-deposition was accelerated significantly on the cationic adsorption film bearing dodecyl groups. It was obvious by ICP-AES analyses that the hydrophobic long-chain dodecyl groups in the adsorption film could promote the adsorption of the negative SnOx colloids on the film surface, followed by much nucleus formation of zerovalent Pd catalysts useful for the electroless plating. The result of our experiment clearly showed that, in addition to electrostatic interaction, van der Waals interaction generating between the hydrophobic long-chain hydrocarbons of the adsorption film and the surfactant improved significantly the adsorption stability of the SnOx colloids, resulting in highly selective Ni-deposition in accord with the photopattern shape of the cationic single-layer adsorption film.