Anionic polymerization and high-vacuum techniques were used to prepare a series of well-defined polyisoprene, polybutadiene, and polystyrene polymacromonomers. The procedure involved (1) the synthesis of styrenic macromonomers in benzene by the selective reaction of the corresponding macroanion with the chlorine of 4-(chlorodimethylsilyl)styrene (CDMSS) and (2) the in situ anionic polymerization of the macromonomer without previous isolation. The synthesis of the macromonomers [polyisoprene macromonomer: 11 samples, weight-average molecular weight (M-w) = 100018,000; polybutadiene macromonomer: 5 samples, M-w = 2000-4000; and polystyrene macromonomer: 2 samples, M_ = 1300 and 3600] was monitored by size exclusion chromatography with refractive index/ultraviolet detectors. Selectivity studies with CDMSS indicated that polybutadienyllithum had the highest selectivity, and polystryryllithium the lowest. From kinetic studies it was concluded that the polymerization half-life times were longer but comparable to those of styrene, and they appeared to only slightly depend on the molecular weight of the macromonomer chain (at least for low degrees of polymerization of the polymacromonomer and for M-w < 7000 for the macromonomer side chain). Dependence on the polymerization degree of the polymacromonomer product was also observed. All the prepared polymacromonomers were characterized by size exclusion chromatography with refractive index, ultraviolet and two-angle laser light scattering detectors, and NMR spectroscopy. (C) 2005 Wiley Periodicals, Inc.