In-situ high-pressure synchrotron angle-dispersive X-ray diffraction for gibbsite (aluminum trihydroxide) was performed at room temperature up to 20 GPa. A pressure-induced phase transition was observed at 2.6 GPa. The new high-pressure phase can be recovered at ambient pressure. Rielveld refinement shows that the new phase of Al(OH)(3) has an orthorhombic structure, spacegroup Pbca, and the lattice parameters at ambient condition are a = 868.57(5) pm, b = 505.21(4) pm, c = 949.54(6) pm, V = 416.67(6) x 10(6) pm(3) with Z = 8. The compressibility of gibbsite and the high-pressure polymorph was analyzed, and their bulk moduli were estimated as 49.8 ± 1.8 and 81.0 ± 5.2 GPa, respectively. First-principles calculations of the high-pressure phase were performed to determine the hydrogen positions and to confirm the structural stability of the new phase.