Highly ordered cage and cylindrical mesoporeous silica monoliths (HOM) with 2- and 3-dimensional (2D and 3D, respectively) structures, mesopore/micropore volumes, and thick-walled frameworks were successfully fabricated by instant direct templating of lyotropic phases of copolymer (EOm-POn-EOm) surfactants. Large cage-like pores with uniform constriction sizes up to 10 nm and open cylindrical channel-like mesopores can be easily achieved by this simple and efficient synthesis design. Our results show that the cage-like pores could be fabricated at relatively lower copolymer concentrations used in the lyotropic phase domains at copolymer/TMOS ratios of 35 wt %. These ordered cage pore architectures underwent transition to opencylindrical pores by increasing the copolymer concentration. High EO/PO block copolymers, in general, were crucially affected on the increase of the interior cavity sizes and on the stability of the cage mesopore characters. However, for F108 (EO141PO44EO141) systems, the fabrication of ordered and stable cage pore monoliths was achieved with significantly higher copolymer concentrations up to 90 wt %. Interestingly, the effective copolymer molecular nature was also observed in the ability to design various ordered mesophase geometries in large domain sizes. Our findings here show evidence that the synthetic strategy provides realistic control over a wide range of mesostructured phase geometries and their extended long-range ordering in the final replicas of the silica monolith frameworks. In addition, the HOM silica monoliths exhibited considerable structural stability against higher thermal temperature (up to 1000 degrees C) and longer hydrothermal treatment times under boiling water and steam. The remarkable structural findings of 3D frameworks, transparent monoliths, and micropores combined with large cage-and cylindrical-like mesopores are expected to find promising uses in materials chemistry.